| 价格 |
|---|
| 0 |
| 试验条件[状态] | ||||
| 测试方法 |
| 测试数据 |
| 数据单位 |
| 物理性能 |
| 模收缩 |
| 1.2-1.4 |
| % |
| 比重 |
| ASTM D-792 |
| 1.34 |
| 自燃性 |
| UL-94 |
| HB |
| 吸水量 |
| 50%相对湿度 |
| ASTM D-570 |
| 0.35 |
| % |
| 吸水量 |
| 24小时浸渍 |
| ASTM D-570 |
| 0.43 |
| % |
| 吸水量 |
| 浸渍平衡点 |
| ASTM D-570 |
| 0.85 |
| % |
| 机械性能 |
| 拉伸强度 |
| 100℃ |
| ASTM D-638 |
| >17 |
| MPa |
| 拉伸强度 |
| -55℃ |
| ASTM D-638 |
| 99 |
| MPa |
| IZOD冲击试验 |
| 缺口-40℃ |
| ASTM D-256 |
| 249 |
| j/m |
| 挠曲系数 |
| 100℃ |
| ASTM D-790 |
| 340 |
| MPa |
| 破裂点拉伸变形量 |
| 122℃ |
| ASTM D-638 |
| >480 |
| % |
| 洛氏硬度M |
| ASTM D-785 |
| 58 |
| 抗拉伸冲击强度 |
| 长试片23℃ |
| ASTM D-1822 |
| 1590 |
| kj/m2 |
| 压缩应力 |
| 23℃,10%变形 |
| ASTM D-695 |
| 52 |
| MPa |
| 洛氏硬度R |
| ASTM D-785 |
| 105 |
| 挠曲系数 |
| -55℃ |
| ASTM D-790 |
| 3260 |
| MPa |
| 拉伸强度 |
| 70℃ |
| ASTM D-638 |
| >29 |
| MPa |
| 破裂点拉伸变形量 |
| 100℃ |
| ASTM D-638 |
| >580 |
| % |
| 挠曲系数 |
| 122℃ |
| ASTM D-790 |
| 230 |
| MPa |
| 破裂点拉伸变形量 |
| 70℃ |
| ASTM D-638 |
| >498 |
| % |
| 破裂点拉伸变形量 |
| -55℃ |
| ASTM D-638 |
| 455 |
| % |
| IZOD冲击试验 |
| 23℃ |
| ASTM D-256 |
| 901 |
| j/m |
| 抗剪强度 |
| 23℃ |
| ASTM D-732 |
| 34 |
| MPa |
| 破裂点拉伸变形量 |
| 23℃ |
| ASTM D-638 |
| 521 |
| % |
| 挠曲系数 |
| 23℃ |
| ASTM D-790 |
| 1280 |
| MPa |
| 挠曲系数 |
| 70℃ |
| ASTM D-790 |
| 650 |
| MPa |
| 压缩应力 |
| 23℃,1%变形 |
| ASTM D-695 |
| 8 |
| MPa |
| 挠曲变形强度 |
| 23℃ |
| ASTM D-790 |
| 40 |
| MPa |
| 挠曲疲劳忍耐限度 |
| 50%RH,23℃,106周期 |
| ASTM D-671 |
| 16 |
| MPa |
| 拉伸强度 |
| 23℃ |
| ASTM D-638 |
| 64 |
| MPa |
| 弹性系数 |
| 23℃ |
| ASTM D-638 |
| 1280 |
| MPa |
| 拉伸强度 |
| 122℃ |
| ASTM D-638 |
| >11 |
| MPa |
| 负载变形量 |
| 140kg/cm2,50℃ |
| ASTM D-621 |
| 3.0 |
| % |
| 电气性能 |
| 容积电阻率 |
| 23℃,0.2%含水量 |
| ASTM D-257 |
| 2.3×1014 |
| Ω.cm |
| 介电因数 |
| 50%RH,23℃,106Hz |
| ASTM D-150 |
| 0.007 |
| 抗电弧 |
| 3.1mm |
| ASTM D-495 |
| 120 |
| sec |
| 介电强度 |
| 瞬间Short time(2.3mm) |
| ASTM D-149 |
| 19.9(2.3) |
| kv/mm |
| 介电常数 |
| 50%RH,23℃,102～106Hz |
| ASTM D-150 |
| 4.1 |
| Ω.cm |
| 热性能 |
| 热畸变温度 |
| 0.5MPa |
| ASTM D-648 |
| 168 |
| ℃ |
| 热畸变温度 |
| 1.8MPa |
| ASTM D-648 |
| 65 |
| ℃ |
| 线性热膨胀系数 |
| 104～160℃ |
| ASTM D-696 |
| 12.8 |
| 10-5m/m℃ |
| 线性热膨胀系数 |
| -40～29℃ |
| ASTM D-696 |
| 9.9 |
| 10-5m/m℃ |
| 线性热膨胀系数 |
| 60～104℃ |
| ASTM D-696 |
| 9.7 |
| 10-5m/m℃ |
| 线性热膨胀系数 |
| 29～60℃ |
| ASTM D-696 |
| 10.6 |
| 10-5m/m℃ |
| 熔点 |
| ASTM D-2133 |
| 175 |
| ℃ |